Low Cement Castables

 

We have a most modern plant for manufacturing low cement castables for various applications including power plants,steel plants,petrochemical plants and refineries,sponge iron units,etc.

 

BRAND NAME PRIL LC – 45 PRIL LC – 60 PRIL LC – 70 PRIL LC – 80 PRIL LC – 90 PRIL LC – 95 PRIL LC – 60S PRIL LC – 70M PRIL LC – 70Li
Type
Nature of Bond
Application Method
Hydraulic
Vibro Casting
Hydraulic
Vibro Casting
Hydraulic
Vibro Casting
Hydraulic
Vibro Casting
Hydraulic
Vibro Casting
Hydraulic
Vibro Casting
Hydraulic
Vibro Casting
Hydraulic
Vibro Casting
Hydraulic
Vibro Casting
GENERAL PROPERTIES
Max grain size , mm
Water required for casting , %

Max Service Temp , °C
RTE at 1000°C , %

6
4.50 – 5.50
1550
0.55
6
4.50 – 5.50
1600
0.60
6
4.50 – 5.50
1600
0.65
6
4.50 – 5.50
1700
0.75
6
4.00 – 5.00
1700
0.85
6
4.00 – 4.70
1800
0.90
6
4.50 – 5.50
1600
0.60
6
4.50 – 5.30
1700
0.65
6
4.50 – 5.50
1650
0.65
CHEMICAL ANALYSIS
Al2O3 , % , min
Fe2O3 , % , max
45.00
1.00
60.00
1.50
70.00
1.50
80.00
1.80
90.00
1.00
94.00
0.30
58.00
1.00
70.00
0.50
70.00
0.85
PHYSICAL PROPERTIES
Bulk Density , gm / cc
after drying at 110°C / 24 hrs , min

CCS, Kg / cm2 , min
after drying at 110 °C / 24 hrs , min

after heating at 800 °C / 3 hrs , min
after heating at 1100 °C / 3 hrs , min
after heating at 1500 °C / 3 hrs , min

2.30

725
825
900
1000

2.60

760
825
900
1000

2.65

760
825
900
1000

2.90

800
900
1000
1150

3.00

950
1000
1100
1200

3.10

1000
1050
1100
1200

2.55

760
800
900
1000

2.60

700
800
950
1100

2.65

700
800
950
1000

THERMAL PROPERTIES
Refractoriness , OC / °C , min
PLC , % , max
after heating at 800°C / 3 hrs
after heating at 1100°C / 3 hrs

after heating at 1500°C / 3 hrs
after heating at 1550°C / 3 hrs

32 OC / 1717±0.20
±0.30
± 1.00
36 OC / 1804±0.20
±0.30
± 1.00
36 OC / 1804±0.20
±0.30
± 1.00
37 OC / 1820±0.20
±0.30

± 1.00
37 OC / 1820±0.20
±0.30

± 0.75
38 OC / 1835±0.20
±0.30

± 0.75
36 OC / 1804±0.20
±0.30
± 0.75
37 OC / 1820±0.20
±0.30

± 0.60
36 OC / 1804±0.20
±0.30

± 0.75