Ultra Low Cement Castables

 

We have a most modern plant for manufacturing low cement castables for various applications including power plants,steel plants,petrochemical plants and refineries,sponge iron units,etc.

BRAND NAME PRIL ULC – 45 PRIL ULC – 60 PRIL ULC – 70 PRIL ULC – 80 PRIL ULC – 90 PRIL ULC – 95 PRIL ULC – 70M PRIL ULC – 80S PRIL ULC – 70Li
Type
Nature of Bond
Application Method
Hydraulic
Vibro Casting
Hydraulic
Vibro Casting
Hydraulic
Vibro Casting
Hydraulic
Vibro Casting
Hydraulic
Vibro Casting
Hydraulic
Vibro Casting
Hydraulic
Vibro Casting
Hydraulic
Vibro Casting
Hydraulic
Vibro Casting
GENERAL PROPERTIES
Max grain size , mm
Water required for casting , %

Max Service Temp , °C

6
4.50 – 5.50
1550
6
4.50 – 5.50
1600
6
4.50 – 5.50
1650
6
4.50 – 5.50
1700
6
4.00 – 5.00
1750
6
4.00 – 5.00
1800
6
4.50 – 5.50
1700
6
4.50 – 5.00
1750
6
4.50 – 5.00
1650
CHEMICAL ANALYSIS
Al2O3 , % , min
Fe2O3 , % , max
CaO, % , max
45.00
1.00
1.00
60.00
1.50
1.00
70.00
1.50
1.00
80.00
1.80
1.00
90.00
1.00
1.00
94.00
0.30
1.00
70.00
0.50
1.00
80.00
0.40
1.00
70.00
0.80
1.00
PHYSICAL PROPERTIES
Bulk Density , gm / cc
after drying at 110°C / 24 hrs , min

CCS, Kg / cm2 , min
after drying at 110 °C / 24 hrs , min

after heating at 800 °C / 3 hrs , min
after heating at 1100 °C / 3 hrs , min
after heating at 1500 °C / 3 hrs , min

2.35

400
825
850
900

2.60

400
825
850
900

2.70

425
800
900
1000

2.90

425
825
1000
1200

3.00

400
1000
1100
1200

3.00

400
700
1000
1250

2.60

450
700
900
1050

2.90

450
700
900
1100

2.70

450
800
900
1000

THERMAL PROPERTIES
Refractoriness , OC / °C , min
PLC , % , max
after heating at 800°C / 3 hrs
after heating at 1100°C / 3 hrs

after heating at 1500°C / 3 hrs
after heating at 1650°C / 3 hrs

32 OC / 1717±0.20
±0.20
± 0.70
36 OC / 1804±0.20
±0.20
± 0.70
36 OC / 1804±0.20
±0.20
± 0.70
37 OC / 1820±0.20
±0.30
±0.80
38 OC / 1835±0.20
±0.30
± 0.80
38 OC / 1835±0.20
±0.30
± 0.80
37 OC / 1820±0.20
±0.30
± 0.50
38 OC / 1835±0.20
±0.30
± 0.50
80
37 OC / 1820±0.20
±0.30
± 0.70